Awọn giredi 310/310S irin alagbara, irin 8.0 * 0.3mm pipọ ọpọn ti o ni okun / ọpọn capillary
Chemcial Tiwqn ti ite 310/310S Irin alagbara, irin
Apapọ kemikali ti ite 310 ati ite 310S irin alagbara, irin ni akopọ ninu tabili atẹle.
Awọn giredi 310/310S irin alagbara, irin 8.0 * 0.3mm pipọ ọpọn ti o ni okun / ọpọn capillary
Tabili 1.Tiwqn kemikali% ti ite 310 ati 310S irin alagbara, irin
| Kemikali Tiwqn | 310 | 310S |
| Erogba | ti o pọju 0.25 | ti o pọju 0.08 |
| Manganese | 2.00 ti o pọju | 2.00 ti o pọju |
| Silikoni | 1.50 ti o pọju | 1.50 ti o pọju |
| Fosforu | ti o pọju 0.045 | ti o pọju 0.045 |
| Efin | ti o pọju 0.030 | ti o pọju 0.030 |
| Chromium | 24.00 - 26.00 | 24.00 - 26.00 |
| Nickel | 19.00 - 22.00 | 19.00 - 22.00 |
Mechanical Properties of ite 310/310S Irin alagbara, irin
Awọn ohun-ini ẹrọ ti ite 310 ati ite 310S irin alagbara, irin ni akopọ ninu tabili atẹle.
Awọn giredi 310/310S irin alagbara, irin 8.0 * 0.3mm pipọ ọpọn ti o ni okun / ọpọn capillary
Tabili 2.Awọn ohun-ini ẹrọ ti ite 310/310S irin alagbara, irin
| Darí Properties | 310/ 310S |
| Ite 0.2 % Ẹri Wahala MPa (iṣẹju) | 205 |
| Agbara Fifẹ MPa (iṣẹju) | 520 |
| Ilọsiwaju % (iṣẹju) | 40 |
| Lile (HV) (o pọju) | 225 |
Awọn ohun-ini ti ara ti Ferritic Alagbara Irin
Awọn ohun-ini ti ara ti ite 310 ati ite 310S irin alagbara, irin ni akopọ ninu tabili atẹle.
Awọn giredi 310/310S irin alagbara, irin 8.0 * 0.3mm pipọ ọpọn ti o ni okun / ọpọn capillary
Tabili 3.Awọn ohun-ini ti ara ti ite 310/310S irin alagbara, irin
| Awọn ohun-ini | at | Iye | Ẹyọ |
| iwuwo |
| 8.000 | Kg/m3 |
| Electrical Conductivity | 25°C | 1.25 | %IACS |
| Itanna Resistivity | 25°C | 0.78 | Micro ohm.m |
| Modulu ti Elasticity | 20°C | 200 | GPA |
| Modulu rirẹ | 20°C | 77 | GPA |
| Iye owo ti Poisson | 20°C | 0.30 |
|
| Yo Rnage |
| 1400-1450 | °C |
| Ooru pato |
| 500 | J/kg.°C |
| Ojulumo oofa Permeability |
| 1.02 |
|
| Gbona Conductivity | 100°C | 14.2 | W/m.°C |
| olùsọdipúpọ ti Imugboroosi | 0-100°C | 15.9 | /°C |
| 0-315°C | 16.2 | /°C | |
| 0-540°C | 17.0 | /°C |